Excellent quality Wolfram Scrap - Niobium Target – HSG Metal
Excellent quality Wolfram Scrap - Niobium Target – HSG Metal Detail:
Product parameters
| Specification | |
| Item | ASTM B393 9995 pure polished niobium target for industry |
| Standard | ASTM B393 |
| Density | 8.57g/cm3 |
| Purity | ≥99.95% |
| Size | according to customer’s drawings |
| Inspection | Chemical composition testing, Mechanical testing, Ultrasonic inspection, Appearance size detection |
| Grade | R04200, R04210, R04251, R04261 |
| Surface | polishing, grinding |
| Technique | sintered, rolled, forged |
| Feature | High temperature resistance, corrosion resistance |
| Application | Superconducting industry, Aerospace aviation, Chmeical Industry, Mechanical |
|
Chemical Composition |
|||
| Grade |
R04200 |
R04210 |
|
| Main element |
Nb |
Bal |
Bal |
| Impurity elements |
Fe |
0.004 |
0.01 |
|
Si |
0.004 |
0.01 |
|
|
Ni |
0.002 |
0.005 |
|
|
W |
0.005 |
0.02 |
|
|
Mo |
0.005 |
0.01 |
|
|
Ti |
0.002 |
0.004 |
|
|
Ta |
0.005 |
0.07 |
|
|
O |
0.012 |
0.015 |
|
|
C |
0.035 |
0.005 |
|
|
H |
0.012 |
0.0015 |
|
|
N |
0.003 |
0.008 |
|
|
Mechanical Property |
|||
|
Grade |
Tensile Strength ≥ Mpa |
Yield Strength ≥ Mpa(0.2% residual deformation) |
Extend Rate % (25.4mm measurement) |
|
R04200 R04210 |
125 |
85 |
25 |
|
Content, Max, Weight % |
||||
|
Element |
Grand: R04200 |
Grand:R04210 |
Grand:R04251 |
Grand:R04261 |
|
Unalloyed Niobium |
Unalloyed Niobium |
(Reactor grade niobium-1% Zirconium) |
(Commercial grade niobium-1% Zirconium) |
|
|
C |
0.01 |
0.01 |
0.01 |
0.01 |
|
O |
0.015 |
0.025 |
0.015 |
0.025 |
|
N |
0.01 |
0.01 |
0.01 |
0.01 |
|
H |
0.0015 |
0.0015 |
0.0015 |
0.0015 |
|
Fe |
0.005 |
0.01 |
0.005 |
0.01 |
|
Mo |
0.01 |
0.02 |
0.01 |
0.05 |
|
Ta |
0.1 |
0.3 |
0.1 |
0.5 |
|
Ni |
0.005 |
0.005 |
0.005 |
0.005 |
|
Si |
0.005 |
0.005 |
0.005 |
0.005 |
|
Ti |
0.02 |
0.03 |
0.02 |
0.03 |
|
W |
0.03 |
0.05 |
0.03 |
0.05 |
|
Zr |
0.02 |
0.02 |
0.8~1.2 |
0.8~1.2 |
|
Nb |
Remainder |
Remainder |
Remainder |
Remainder |
Product technology
The vacuum electron beam melting process produces niobium plates. The unforged niobium bar is first smelted into a niobium ingot through a vacuum electron beam melting furnace. It is usually divided into single smelting and multiple smelting. We usually use twice smelted niobium ingots. Depending on the product requirements, we can perform more than two smelting.
Application
Superconducting industry
Used to produce niobium foil
Heat shield in high temperature furnace
Used to produce niobium welded pipe
Used in the production of human implants.
Product detail pictures:
Related Product Guide:
Our growth depends on the superior equipment ,exceptional talents and continuously strengthened technology forces for Excellent quality Wolfram Scrap - Niobium Target – HSG Metal , The product will supply to all over the world, such as: Iran, Turkey, Stuttgart, Our products and solutions are sold to the Middle East, Southeast Asia, Africa, Europe, America and other regions, and are favorably appraised by clients. To benefit from our strong OEM/ODM capabilities and considerate services, be sure to contact us today. We will sincerely create and share success with all clients.
By Maria from Provence - 2017.08.16 13:39
The quality of the products is very good, especially in the details, can be seen that the company work actively to satisfy customer's interest, a nice supplier.
By Rosemary from Bahrain - 2018.07.26 16:51
Related products
-
Molybdenum Scrap - High Pure 99.95% And High Q...
Product Parameters Product Name Best price pure molybdenum tube with various specifications Material pure molybdenum or molybdenum alloy Size reference the below details Model Number Mo1 Mo2 Surface hot rolling, cleaning, polished Delivery time 10-15 working days MOQ 1 kilograms Used Aerospace industry, Chemical equipment industry The specification would be changed by the customers’ requirements. Regular size range Diameter (mm) Wall thickness (mm) Len...
-
Ferro Niobium - Factory Price Used For Superco...
Product Parameters Commodity Name Niobium Wire Size Dia0.6mm Surface Polish and bright Purity 99.95% Density 8.57g/cm3 Standard GB/T 3630-2006 Application Steel, superconducting material, aerospace, atomic energy, etc Advantage 1) good superconductivity material 2) Higher melting point 3) Better Corrosion Resitance 4) Better wear-resisting Technology Powder Metallurgy Lead time 10-15 days Products Description Niobium wi...
-
2022 Good Quality Ferro Niobium Lumps - High Q...
Product Parameters Product Name Polished Pure niobium Seamless Tube for Piercing Jewelry kg Materials Pure Niobium and Niobium Alloy Purity Pure niobium 99.95%min. Grade R04200, R04210, Nb1Zr (R04251 R04261), Nb10Zr, Nb-50Ti etc. Shape Tube/pipe, round, square, block, cube, ingot etc. customized Standard ASTM B394 Dimensions Accept customized Application Electronic industry, steel industry, chemical industry, optics, gemstone manufacturing, superconducting technology, aerospa...
-
Indium Ingot - high purity round shape 99.95% ...
Product parameters Brand Name HSG Metal Model Number HSG-moly target Grade MO1 Melting point(℃) 2617 Processing Sintering/ Forged Shape Special Shape Parts Material Pure molybdenum Chemical Composition Mo:> =99.95% Certificate ISO9001:2015 Standard ASTM B386 Surface Bright and Ground Surface Density 10.28g/cm3 Color Metallic Luster Purity Mo:> =99.95% Application PVD coating film in glass industry , ion plating Advantage High Temperature Resistance, Hig...
-
Fast delivery Steel Making Molybdenum Bar - 0....
Molybdenum wire advantage 1. Molybdenum wire high pricision,line diameter tolerance control at less than 0 to 0.002mm 2. The ratio of breaking wire low,processing rate is high,good performance and good price. 3. Can finish the stable long time continuous processing. Products Description Edm molybdenum Moly wire 0.18mm 0.25mm Molybdenum wire(spray moly wire)is mainly used for auto parts spraying,such as piston ring,synchronizer rings,shift elements,etc.Molybdenum spray wire is also used in rep...
-
Ferro Vanadium Prijs - Ferro Vanadium – ...
Specification of Ferrovanadium Brand Chemical Compositions (%) V C Si P S Al Mn ≤ FeV40-A 38.0~45.0 0.60 2.0 0.08 0.06 1.5 — FeV40-B 38.0~45.0 0.80 3.0 0.15 0.10 2.0 — FeV50-A 48.0~55.0 0.40 2.0 0.06 0.04 1.5 — FeV50-B 48.0~55.0 0.60 2.5 0.10 0.05 2.0 — FeV60-A 58.0~65.0 0.40 2.0 0.06 0.04 1.5 — FeV60-B 58.0~65.0 0.60 2.5 0.10 0.05 2...